PE polyethylene additive flame retardant chemical 6-8% dosing in pe blowing and yarn CAS NO.1309-64-4

Name: PE polyethylene additive flame retardant chemical 6-8% dosing in pe blowing and yarn
SKU: 1309-64-4
Availability: InStock

1, The final products using this flame retardant will be no frost and whity.

2, Low additive so save the cost. It can be added directly in PE, reduce the process stage so save cost.

3, It meet the standard RoHS, no contain PBB, PBDE, no powder and no pollution.

4, Good heat stability and suitable for process in high temperature (≥200°C)

5, The density for final products is ≤1.0; The density for Br flame retardant is about 1.3.

6, Good physical performance and stay the same physical performance as resin (consistency with resin)

7, Good fluxility in process

HDPE,LDPE,EVA RESIN(% wt)	Adding percent(% wt)	FR level
Drawbench,Safetynet,Blowing, 94—92	6—8	UL94 V2
Tarp, Christmasdecoration, Sheet, 92—90	8—10	UL94 V2
Injection, extrusion: 90—85	10—15	UL94 V2

Technology Data:

Feature	Norm	Unit	6001	6001B	6001E
Density	ASTN D-792	g/cm3	0.97	0.98	0.96
melt index (190℃/2.16kgs)	ASTN D-1238	g/10min	30	15	50
Thermal deformation Temperature (0.45mpa)	ASTN D-648	℃	——	——	——
tensile yield strength	ASTN D-638	mpa	10	10	10
elongation at break	ASTN D-638	%	150	300	150
bending strength	ASTN D-790	mpa	8	8	8
bending modulus	ASTN D-790	mpa	165	175	165
notch impact strength	ASTN D-256	j/m	120	460	200
flame retardant	UL94 (E253482)	1.5mmv2/3.0mmv2	OK	OK	OK
Color	——	——	Green/white	Green/white	Green/white

Injection Technique:

The drying temperature/time	Injection Temperature	Injection speed	Mold temperature
——	180-160℃	50-80%	40-70℃